Primary sealant
 Primary butyl sealant Kemerling CG 115 - made on the basis of synthetic rubber without the use of solvent. Is a solid mass, treatment which is only possible at elevated temperatures
| Basis |
Synthetic rubber |
| Color |
Black |
| Consistency |
Solid mass |
| Density |
~ 1.05 (kg/dm3) |
| Vapor permeability |
0.17 g/m2 day |
| Surface Treatment |
Surface on which the sealant is applied must be clean, dry and free from dust and grease |
| Application |
Sealant CG 115 comes ready to use. Applied with butlekstrudera (temperature of 110 ° C to 130 ° C) or device for the application of butyl tape |
| Storage |
1 year in cool, dry |
| Packing |
Cylinder in a cardboard box on 2,2 kg |
 Butylver is the solvent-free, single-component sealant specially developed for use in the primary sealing of multiple glass panes. Prevents efficiently against the entry of water vapor inside of multiple glass panes, characterized by the high wear resistance and excellent adhesive characteristics with respect to glass and aluminum.
| Substrate |
Polyisobutylene |
| Mixture color |
Black |
| Consistence |
Solid mass |
| Density |
About 1.08 kg/dm3 |
| Vapor permeability |
0.11 g / m2 day |
| Surface treatment |
The sealed surface should be clean, dry and degreased |
| Application |
Butylver should be used at working temperature of 130°-150°С using the appropriate extruders |
| Storage |
1 year in the dry and ventilated spaces |
| Package |
Cylinders: 2.5 and 7 kg |
Double-faced tapes of primary sealing
Tape manufactured by Garbalinski GmbH (Germany)
The double-faced tape manufactured of the butyl rubber reinforced by special fabric. Purpose of a tape is an initial gluing of multiple glass panes. Dimension: 4mm x 30m.
Technical characteristics
| Glue |
Butyl rubber |
| Carrier (reinforcing agent) |
Special fabric |
| Thickness |
0.6 mm |
| Protection |
White siliconized paper 120 g/m |
| Test for break-off from the steel surface at 180° for 24 hours by rules of AFERA 5001 |
16 N / 25 mm |
| Shearing test at 23oС 1kg/625mm2 |
>10 hours |
| Temperature interval |
- 40°С - 90°С |
Features of product: High resistance to the ultraviolet radiation, aging and temperature extremes. High final adhesion and shearing force index.
Double-faced Scotch tape RS.
Double-faced adhesive semitransparent tape consisting of nonwoven paper substrate and acrylic adhesive. Dimension: 4mm x 50m.
Technical characteristics:
| Glue |
synthetic rubber (transparent, without plasticizers) |
| Carrier (reinforcing agent) |
nonwoven material |
| Thickness |
0.6 mm |
| Protection |
siliconized brown paper 120 g/m |
| Test for break-off from the steel surface at 180° for 24 hours by rules of AFERA 5001 |
14N / 25 mm |
| Shearing test at 23oС 1kg/625mm2 |
>10.5 hours |
| Temperature interval |
from -40 to +120 С |
Features of product:
The tape is suitable for the manual application, high resistance to aging and ultraviolet radiation. High adhesion to materials of multiple glass panes.
Double-faced tape of Russian manufacture for primary sealing
Description
Double-faced adhesive tape 4mm x 50m on the nonwoven substrate (on basis of paper fibers), semitransparent.
Range of application
For primary sealing (for fastening of the spacer) |
|
Features
-
tape carrier — paper fibers impregnated with glue which provides the high strength characteristics
-
tape is suitable for manual application because it is easily torn
-
rubber glue provides a high degree of tape resistance to moisture, abrupt temperature changes (cold-resistant)
Technical characteristics
| nonwoven material |
| synthetic rubber (transparent, without plasticizers) |
| brown siliconized paper |
| Characteristic |
Average value |
units |
| Thickness of glue film |
135 – 150 |
µ (мкм) |
| protective layer |
76 – 80 |
units |
| Breaking strength |
11 ± 3 |
N/cm |
| Tension before breaking |
2 |
% |
| Tear at 180° |
12.1 ± 3.7 |
N/cm |
| Static load |
>90 |
hours |
| adhesiveness (rolling ball tack) |
7 ± 4 |
cm |
| Standard dimension |
4mm x 50m |
|
|
|